ULTEM™ HU1110 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zWr5Yw_ULTEMHU1110resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Enhanced flow Polyetherimide (Tg 217C). RoHS compliant. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant. EtO and steam sterilizable. UL94 V0 and 5VA listed. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 340°C/5.0 kg | 12.0 | cm³/10min | ISO 1133 |
| 360°C/5.0 kg | 21.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 1.2 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.65 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 145 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 110 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 6.0 | % | ISO 527-2/5 |
| Fracture | 60 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 3300 | MPa | ISO 178 |
| Flexural Stress | 140 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 10.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact 3 | ISO 180/1A | ||
| -30°C | 4.0 | kJ/m² | ISO 180/1A |
| 23°C | 4.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 100 mm span 4 | 200 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span 5 | 185 | °C | ISO 75-2/Ae |
| 1.8 MPa, unannealed, 64.0mm span 6 | 210 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 210 | °C | ISO 306/A50 |
| -- | 200 | °C | ISO 306/B50 |
| -- | 205 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 5.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flow : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 5.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Horizontal : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.26 | W/m/K | ISO 8302 |
| RTI Elec | 170 | °C | UL 746 |
| RTI Imp | 170 | °C | UL 746 |
| RTI | 170 | °C | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index (3.20 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 47 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 332 - 399 | °C | |
| Middle Temperature | 338 - 399 | °C | |
| Front Temperature | 343 - 399 | °C | |
| Nozzle Temperature | 343 - 399 | °C | |
| Processing (Melt) Temp | 349 - 399 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 sp=62mm |
| 3 . | 80*10*4 |
| 4 . | 120*10*4 mm |
| 5 . | 120*10*4 mm |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® BGV HZ 15 Natural | Radici Plastics | Nylon 6 | Radilon® |
| Moplen RP346R | HMC Polymers | PP Random Copolymer | Moplen |
| Flontech® FT-BRR60-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Generic Nylon 66 - Glass Bead\Glass Fiber | Generic | Nylon 66 | Generic |
| Sarlink® TPE FM-2166 | Teknor Apex Company | TPE | Sarlink® TPE |