Glass-fibre reinforced phenolic moulding compound Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties Primary application(s): Commutators This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.80 to 1.90 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 to 1.00 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow 1 | 0.20 to 0.40 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | < 0.20 | % | ISO 62 |
| Post Shrinkage 2 | < 0.050 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| Compression Molded | 6000 to 8000 | MPa | |
| Injection Molded | 7000 to 9000 | MPa | |
| Tensile Stress | ISO 527-2 | ||
| Compression Molded | 60.0 to 80.0 | MPa | |
| Injection Molded | 70.0 to 90.0 | MPa | |
| Flexural Modulus | ISO 178 | ||
| Compression Molded | 13000 to 17000 | MPa | |
| Injection Molded | 14000 to 18000 | MPa | |
| Flexural Stress | ISO 178 | ||
| Compression Molded | 100 to 120 | MPa | |
| Injection Molded | 140 to 160 | MPa | |
| Compressive Stress | 200 to 250 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| Compression Molded | 2.0 to 4.0 | kJ/m² | |
| Injection Molded | 2.0 to 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| Compression Molded | 5.0 to 7.0 | kJ/m² | |
| Injection Molded | 7.0 to 9.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | > 180 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 140 to 160 | °C | ISO 75-2/C |
| CLTE - Flow (50 to 150°C) | 1.0E-5 to 1.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.40 to 0.60 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 to 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+12 to 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 20 to 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 8.00 6.00 | ||
| 1 MHz | 6.00 4.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.010 to 0.050 | ||
| 1 MHz | 0.020 to 0.030 | ||
| Arc Resistance | PLC 4 | ASTM D495 | |
| Comparative Tracking Index | > 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Tested by Synres-Almoco) | V-0 | UL 94 | |
| Glow Wire Flammability Index | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 960 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| 2 . | 168 h / 110°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PC GN5002RFP | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| SUSTAMID 6G M | Röchling Sustaplast SE & Co. KG | Nylon 6 | SUSTAMID |
| Badaprene® TPV 90A 1076 UV | Bada AG | PP+EPDM | Badaprene® |
| POLYfill PPC GF5020 PB | Polykemi AB | PP Copolymer | POLYfill |
| Medalist® MD-12170H (PRELIMINARY DATA) | Teknor Apex Company | TPE | Medalist™ |