OPTODYNE™ UV-3000
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | DAIKIN AMERICA, INC. |
| Trademark: | OPTODYNE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zVmIHi_OPTODYNE-UV-3000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Optodyne UV-3000 is a single component, acrylic-based UV curable adhesive designed for bonding optical connectors, lenses, prisms and other optical components. Its exceptional strength, combined with its unique index matching capability, make the Optodyne Series of adhesives superior in many respects:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | Internal Method | ||
| -- 1 | 1.07 | g/cm³ | |
| -- 2 | 1.14 | g/cm³ | |
| Molding Shrinkage - Flow 3 | 6.0 | % | Internal Method |
| Water Absorption 4(24 hr) | 0.11 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 5(Shore D) | 57 | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Continuous Use Temperature 6 | 100 | °C | Internal Method |
| Glass Transition Temperature 7 | 100 | °C | Internal Method |
| CLTE - Flow 8 | 6.2E-5 | cm/cm/°C | Internal Method |
| Flammability | Nominal Value | Unit | |
|---|---|---|---|
| Flash Point - Before Cure | 132 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Temperature of Intial Weight Loss - 5% Weight Loss 9 | 328 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 10 | 1.475 | Internal Method | |
| Transmittance 11 | 92.5 | % | Internal Method |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity 12 | 1600 | cP | Internal Method |
| Note Message | |
|---|---|
| 1 . | Before Cure, 25°C |
| 2 . | After Cure, 25°C |
| 3 . | After Cure |
| 4 . | After Cure |
| 5 . | After Cure |
| 6 . | After Cure |
| 7 . | After Cure |
| 8 . | After Cure |
| 9 . | After Cure |
| 10 . | Before Cure, 25°C |
| 11 . | After Cure |
| 12 . | Before Cure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PC PC1800 resin | SABIC Innovative Plastics Asia Pacific | PC | SABIC® PC |
| Tenite™ Acetate 132E5243225 Clear, Trsp | Eastman Chemical Company | CA | Tenite™ Acetate |
| Vipel® F701-FBY-45 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| TOTAL Polypropylene PPC 6742 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Formolene® DB5305A | Formosa Plastics Corporation, U.S.A. | UHMWPE | Formolene® |