PRE-ELEC® PP 1383
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zVhitW_PRE-ELEC-PP-1383.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® PP 1383 is a conductive polypropylene compound with high MFI. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® PP 1383 has an excellent balance of mechanical properties and is easy to injection mould. Typical applications include injection moulded technical parts. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.996 | g/cm³ | ASTM D792 |
| -- | 0.990 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 14 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 1.2 to 1.4 | % | ASTM D955, ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shore A | 95 | ||
| Shore D | 65 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 25.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 4.00 mm | 1310 | MPa | ASTM D790 |
| 4.00 mm | 1300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1 | |||
| -20°C | 8.4 | kJ/m² | ASTM D256 |
| -20°C | 9.0 | kJ/m² | ISO 179 |
| 23°C | 12 | kJ/m² | ISO 179 |
| 23°C | 11 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 2 | |||
| -20°C | No Break | ASTM D256, ISO 179 | |
| 23°C | No Break | ISO 179, ASTM D256 | |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | 4.20 | kJ/m² | |
| 23°C, 4.00 mm | 8.41 | kJ/m² | |
| Notched Izod Impact Strength 3 | ISO 180 | ||
| -20°C | 5.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Unnotched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | 54.6 | kJ/m² | |
| 23°C, 4.00 mm | 60.9 | kJ/m² | |
| Unnotched Izod Impact Strength 4 | ISO 180 | ||
| -20°C | 55 | kJ/m² | |
| 23°C | 59 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 100 | °C | ASTM D648B, ISO 75-2/Bf |
| Vicat Softening Temperature | |||
| -- | 149 | °C | ASTM D1525 5 |
| -- | 150 | °C | ISO 306/A50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+3 | ohms | ESD STM11.11, IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+2 | ohms·cm | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 200 to 250 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 80.0 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| 3 . | 4 mm thickness |
| 4 . | 4 mm thickness |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2922-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TEREZ PA 6 7530 GF 30 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| VECTRA® E440i | Celanese Corporation | LCP | VECTRA® |
| Braskem PP TR3350MS | Braskem America Inc. | PP Random Copolymer | Braskem PP |
| LNP™ LUBRICOMP™ REL22 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |