CONTINUUM™ DMDE-6620 NT 7 BIMODAL
| Category: | HDPE , Bimodal Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | CONTINUUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zU9HRb_CONTINUUMDMDE6620NT7BIMODAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
DMDE-6620 NT 7 Bimodal High Density Polyethylene Resin is produced by UNIPOL™ II process technology. This resin is a high stiffness resin with superior top-load performance in conjunction with excellent environmental stress crack resistance and excellent gas barrier properties. DMDE-6620 NT 7 is specifically designed for use in multiple types of blow molding processes, producing containers up to 20 gallons in size, which require superior top-load combined with excellent environmental stress crack resistance and gas barrier properties. This product offers excellent processability with low plate out properties. This product is especially well suited for containers used to package household industrial chemicals (e.g. detergents, and fabric softeners), toiletries and cosmetics (e.g. shampoos, creams, lotions, etc.), health, pharmaceutical, and food products.
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.28 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 27 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | ASTM D1693 | ||
| 50°C, 10% Igepal, F50 | 220 | hr | ASTM D1693 |
| 50°C, 100% Igepal, F50 | > 1100 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 59 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 28.0 | MPa | ASTM D638 |
| Fracture | 18.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 8.0 | % | ASTM D638 |
| Fracture | 670 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 1170 | MPa | ASTM D790B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 82.0 | °C | ASTM D648 |
| Brittleness Temperature | -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 131 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 133 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 121 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D 4976 进行模塑和测试。 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MEGOLON™ S336 | AlphaGary | TP, Unspecified | MEGOLON™ |
| TES J-4/35 BK223 | Techmer Engineered Solutions | Nylon 612 | TES |
| NORYL™ WCP921 resin | SABIC Innovative Plastics Asia Pacific | PPE+TPE | NORYL™ |
| Hostaform® S 9364 WS 10/1570 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Hostacom ERC 342N E1 C11306 | LyondellBasell Industries | PP Copolymer | Hostacom |