Trexlink™ 6770 GM
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | Trexlink™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zU44VZ_Trexlink-6770-GM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Trexlink ™ 6770 GM is a highly engineered Thermoplastic Elastomer for use in applications requiring integrally colored material. This material is UV stabilized and can be pre-colored in most Automotive Interior or other colors. It can be easily processed by injection molding or blow molding. Applications include critical color matched Automotive components such cup holders, mats, seals, soft seat trim. Also works well for two-shot molding or over-mold components such as grips and handles |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 5 sec, Injection Molded) | 71 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Across Flow 1(100% Strain) | 2.20 | MPa | ISO 37 |
| Tensile Stress - Across Flow 2(Yield) | 5.20 | MPa | ISO 37 |
| Tensile Elongation - Across Flow 3(Break) | 650 | % | ISO 37 |
| Tear Strength - Across Flow 4 | 24 | kN/m | ISO 34-1 |
| Compression Set 5(70°C, 22 hr) | 35 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 6(135°C, 1000 hr) | -5.0 | % | ISO 188 |
| Change in Tensile Strain at Break in Air 7(135°C, 1000 hr) | -2.0 | % | ISO 188 |
| Additional Information |
|---|
| Change in Color, SAE J1885, 1240.8kJ/m² exposure: <3.0 delta E |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 177 - 216 | °C | |
| Middle Temperature | 177 - 216 | °C | |
| Front Temperature | 177 - 216 | °C | |
| Nozzle Temperature | 188 - 221 | °C | |
| Processing (Melt) Temp | 182 - 221 | °C | |
| Mold Temperature | 10.0 - 65.6 | °C | |
| Back Pressure | 0.0689 - 1.03 | MPa | |
| Screw Speed | 100 - 200 | rpm | |
| Screw L/D Ratio | 20.0:1.0 |
| Note Message | |
|---|---|
| 1 . | Type 1 |
| 2 . | Type 1 |
| 3 . | Type 1 |
| 4 . | Method B, right-angle specimen (cut) |
| 5 . | Type a |
| 6 . | Method B |
| 7 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD 805 | RTP Company | Acetal (POM) Copolymer | RTP |
| Radilon® A 50W 100 M NAT 5770 | Radici Plastics | Nylon 66 | Radilon® |
| Sylvin 8200-93UV Clear Yellow 4199 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 3105 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| SABIC® PC PC0800 resin | SABIC Innovative Plastics Asia Pacific | PC | SABIC® PC |