Polytron® P35B03
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | Polytron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zSCc1T_Polytron-P35B03.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A CHEMICALLY COUPLED 35% LONG GLASS FIBERS REINFORCED BLACK POLYPROPYLENE, HEAT STABILIZED FOR INJECTION MOULDING APPLICATION. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.14 | % | ASTM D955 |
| -- | 0.14 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 110 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 6000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 160 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 160 | J/m | ASTM D256 |
| 23°C | 16 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 150 | °C | ASTM D648, ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 303 H TFE 15 | RTP Company | PC | RTP |
| ADENE BCZB | A.D. Compound spa | PP Homopolymer | ADENE |
| Grivory® HT3Z LF black 9564 | EMS-GRIVORY | Nylon 10T/X | Grivory® |
| Karina BLACK PVC COMPOUND 651-48/1-B-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ VERTON™ MV008SU compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ VERTON™ |