RTP 3400 FC-130
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zS8YQU_RTP-3400-FC-130.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. Mineral Reinforced - UL94 V-0 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.86 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.050 - 0.30 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ASTM D638 |
| Tensile Strength | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 0.75 | % | ASTM D638 |
| Flexural Modulus | 9650 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 32 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 80 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 288 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 1(in Oil) | 38 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.80 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.025 | ASTM D150 | |
| Arc Resistance | 244 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| Dew Point: -20°FTensile Elongation, ASTM D638: 0.5 to 1%Volume Resistivity, ASTM D257: >1E+15 ohm-cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 8.0 | hr | |
| Processing (Melt) Temp | 363 - 399 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Injection Pressure | 68.9 - 124 | MPa |
| Injection instructions |
|---|
| The key to successfully molding this material is to start mold open cycles as soon as the screw reaches its retracted position. |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DENITER 3015 | Vamp Tech | PBT | DENITER |
| Kingfa JH960 6610 | Kingfa | PC+ABS | Kingfa |
| PENTAMID B GV30 H natur | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |
| PRIMACOR™ 3540 | The Dow Chemical Company | EAA | PRIMACOR™ |
| Kangxi® FRABSMIV-0 | Wuxi Kangxi Plastics Technology Co.,Ltd. | ABS | Kangxi® |