PP Random Copolymer for Injection Molding

Characteristics

The KPOL® resin is specially developed for producing injection molded articles with high clarity and also has better impact properties than homo PP counterparts.

Good Chemical Resistance, High Clarity, Good Impact Resistance, Good Processability, Medium Rigidity.

KPOL - K-PPR 26.0 is suitable for Food contact application.

Applications

Containers with high transparency, Containers for freezer, Housewares, Lids and Closures and Battery Cases.

Injection Molding and Injection Stretch Blow Molding of bottles and packages.

General Information
Additive	Antioxidant
Features	Antioxidant Food Contact Acceptable Good Chemical Resistance Good Impact Resistance Good Processability High Clarity Medium Rigidity Random Copolymer
Uses	Battery Cases Bottles Closures Containers Food Containers Household Goods Lids Packaging
Agency Ratings	FDA 21 CFR 177.1520
Appearance	Clear/Transparent
Processing Method	Injection Molding Stretch Blow Molding

Physical	Nominal Value	Unit	Test Method
Density	0.902	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	26	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	83		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield)	32.0	MPa	ASTM D638
Tensile Elongation ²(Break)	13	%	ASTM D638
Flexural Modulus - 1% Secant	1100	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	50	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	77.0	°C	ASTM D648
Vicat Softening Temperature	130	°C	ASTM D1525 ³

Note Message
1 .	Type IV, 50 mm/min
2 .	Type IV, 50 mm/min
3 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
PRIMALLOY® B1922	Mitsubishi Chemical Performance Polymers, Inc.	TPE	PRIMALLOY®
XANTAR® LDS 3710	Mitsubishi Engineering-Plastics Corp	PC+ABS	XANTAR® LDS
Dugdale PVC Flexible Extrusion - Shore A 83 Compound	Dugdale Plc	PVC, Flexible	Dugdale PVC
Laril 13 G/20-V1	LATI S.p.A.	PPE+PS	Laril
LEXAN™ 103 resin	SABIC Innovative Plastics	PC	LEXAN™