POCAN® B 4235 Z 000000

Category:	PBT , Polybutylene Terephthalate
Manufacturer:	LANXESS Corporation
Trademark:	POCAN®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	zQalQ6_POCANB4235Z000000.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
PBT, 30 % glass fibers, injection molding, flame retardant, improved impact strength

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Additive	Flame retardancy
Features	Impact resistance, good Flame retardancy
Agency Ratings	EC 1907/2006 (REACH)
Processing Method	Injection molding
Resin ID (ISO 1043)	PBT GF FR (17)

Physical	Nominal Value	Unit	Test Method
Density (23°C)	1.62	g/cm³	ISO 1183
Apparent Density	0.80	g/cm³	ISO 60
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg)	26.0	cm³/10min	ISO 1133
Molding Shrinkage			ISO 2577
Vertical flow direction : 250°C, 2.00mm ¹	0.90	%	ISO 2577
Vertical flow direction : 120°C, 4 hours, 2.00mm ²	0.10	%	ISO 2577
Flow direction : 250°C, 2.00mm ³	0.30	%	ISO 2577
Flow direction : 120°C, 4 hours, 2.00mm ⁴	0.10	%	ISO 2577
Water Absorption			ISO 62
Saturated, 23°C	0.40	%	ISO 62
Equilibrium, 23°C, 50% RH	0.10	%	ISO 62
Viscosity Number (Reduced Viscosity)	83.0	ml/g	ISO 1628

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	185	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	10000	MPa	ISO 527-2/1
Tensile Stress (Break, 23°C)	125	MPa	ISO 527-2/5
Tensile Strain (Break, 23°C)	2.8	%	ISO 527-2/5
Flexural Modulus ⁵(23°C)	9700	MPa	ISO 178/A
Flexural Stress ⁶(23°C)	210	MPa	ISO 178/A
Flexural Strain at Flexural Strength ⁷(23°C)	3.2	%	ISO 178/A

Additional Information	Nominal Value		Test Method
ISO Shortname	PBT, GFHMPR, 09-100, GF30		ISO 7792

Injection	Nominal Value	Unit	Test Method
Residual Moisture Content	0.0 - 0.020	%	Karl Fisher

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	< 10	kJ/m²	ISO 179/1eA
23°C	< 10	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	60	kJ/m²	ISO 179/1eU
23°C	60	kJ/m²	ISO 179/1eU
Notched Izod Impact			ISO 180/1A
-40°C	< 10	kJ/m²	ISO 180/1A
-30°C	< 10	kJ/m²	ISO 180/1A
23°C	< 10	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength			ISO 180/1U
-30°C	55	kJ/m²	ISO 180/1U
23°C	55	kJ/m²	ISO 180/1U

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	220	°C	ISO 75-2/B
1.8 MPa, not annealed	200	°C	ISO 75-2/A
8.0 MPa, not annealed	130	°C	ISO 75-2/C
Vicat Softening Temperature	210	°C	ISO 306/B120
Ball Pressure Test (210°C)	Pass		IEC 60695-10-2
Melting Temperature ⁸	225	°C	ISO 11357-3
Linear thermal expansion coefficient			ISO 11359-2
Flow : 23 to 55°C	2.0E-5	cm/cm/°C	ISO 11359-2
Lateral : 23 to 55°C	1.0E-4	cm/cm/°C	ISO 11359-2

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	175	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
0.750 mm	V-2		UL 94
1.50 mm	V-0		UL 94
3.00 mm	5VA		UL 94
Glow Wire Flammability Index (2.00 mm)	960	°C	IEC 60695-2-12

Injection	Nominal Value	Unit	Test Method
Drying Temperature - Circulation Dryer	120	°C
Drying Time - Circulation Dryer	4.0 - 8.0	hr
Processing (Melt) Temp	240 - 260	°C
Mold Temperature	80.0 - 100	°C

Note Message
1 .	60x60x2mm, 80°C MT, 600 bar
2 .	60x60x2mm
3 .	60x60x2mm, 80°C MT, 600 bar
4 .	60x60x2mm
5 .	2.0 mm/min
6 .	2.0 mm/min
7 .	2 mm/min
8 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
Marlex® HHM 4903	Chevron Phillips Chemical Company LLC	HDPE	Marlex®
Durolon® VR2000 CR010	Unigel Plásticos	PC	Durolon®
Hostacom SP 98/F	LyondellBasell Industries	PP Copolymer	Hostacom
Hostacom M4 U02 200007	LyondellBasell Industries	PP Homopolymer	Hostacom
Delon 6055	Shanghai Lin Gen Rubber Materials Co., Ltd.	TEEE	Delon