Arylmax® K7500WC30
| Category: | PAEK , Polyaryletherketone |
| Manufacturer: | Polymics, Ltd. |
| Trademark: | Arylmax® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zQGPO9_Arylmax-K7500WC30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Arylmax® K7500WC30 is a Polyaryletherketone (PAEK) product. It is available in North America. Primary characteristic: wear resistant. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ASTM D638 |
| Tensile Strength (Break) | 130 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 9510 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 210 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 170 | °C | DSC |
| Melting Temperature | 353 | °C | DSC |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 180 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 380 | °C | |
| Middle Temperature | 380 | °C | |
| Front Temperature | 380 | °C | |
| Nozzle Temperature | 380 | °C | |
| Mold Temperature | 200 to 210 | °C | |
| Injection Rate | Fast | ||
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMTOUGH RZ236 | Polyram Ram-On Industries | PC | RAMTOUGH |
| CYCOLAC™ X11 resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| GERMAMID 6 VO | Kunststoff-Kontor-Hamburg GmbH | Nylon 6 | GERMAMID |
| EPAMOULD 274D12 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |
| LEXAN™ HFD4413 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |