| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | 4Plas |
| Trademark: | 4LAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zPmsHt_4LAC-25H23100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4LAC 25H23100 is a MFI 20 to 22 FR-V0 ABS |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (270°C/2.16 kg) | 22 | g/10 min | ISO 1133 |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 102 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2300 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 44.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 40 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 118 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 104 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 124 | °C | ISO 306/B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| High Amp Arc Ignition (HAI) (1.57 mm) | 10.0 | UL 746 | |
| Hot-wire Ignition (HWI) (1.57 mm) | 57 | sec | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 190 - 230 | °C | |
| Mold Temperature | 50.0 - 60.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 50.0 - 100 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 30 - 50 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 TFE 18 SI 2 | RTP Company | PC | RTP |
| Moplen EP500V | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Moplen EP2X30F | Shazand (Arak) Petrochemical Corporation | PP Random Copolymer | Moplen |
| Jamplast Ex-17 ABS | Jamplast, Inc. | ABS | Jamplast |
| Osterlene® LLDO-1.0-.920 | Osterman & Company | LLDPE | Osterlene® |