12% Mica Reinforced, Chemically Coupled, Impact Modified Polypropylene Colors Available Meets GMP.PP.028 |
General Information | |
---|---|
Filler / Reinforcement |
|
Additive |
|
Features |
|
Appearance |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 0.998 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
Molding Shrinkage - Flow (3.18 mm) | 1.0 | % |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength (Yield) | 24.1 | MPa | ASTM D638 |
Tensile Elongation (Break) | > 10 | % | ASTM D638 |
Flexural Modulus | 1650 | MPa | ASTM D790 |
Flexural Strength | 31.0 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (3.18 mm) | 80 | J/m | ASTM D256 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 65.6 | °C | ASTM D648 |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
VAMPAMID 66 0023 V0 H GW | Vamp Tech | Nylon 66 | VAMPAMID |
Diakon® LH752 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
Epoxies, Ect. 10-3008 | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
Karina IVORY PVC COMPOUND -E 90900-35/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
Plaslube® PA6 TS18 | Techmer Engineered Solutions | Nylon 6 | Plaslube® |