3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 6302
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | 3M Advanced Materials Division |
| Trademark: | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zPB20v_3M-Dyneon-TFM-Modified-PTFE-Compound-TFM-6302.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 3M™ Dyneon™ TFM™ Modified PTFE Compound 6302 is a Polytetrafluoroethylene (PTFE) product filled with 10% graphite fiber. It can be processed by compression molding or sintering and is available in Europe or North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.15 | g/cm³ | ASTM D4745-06 |
| Apparent Density | 0.75 | g/cm³ | ASTM D4894 |
| Molding Shrinkage - Flow | 3.4 | % | ASTM D4894-07 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness 1(Shore D) | 68 | DIN 53505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Break) | 23.5 | MPa | ASTM D4745-06 |
| Tensile Elongation 3(Break) | 380 | % | ASTM D4745-06 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | 50.0 | MPa | |
| Compression Molding Temperature | 23 to 26 | °C | |
| Sintering Temperature | < 365 | °C |
| Note Message | |
|---|---|
| 1 . | Measured on sintered moldings |
| 2 . | Measured on sintered moldings |
| 3 . | Measured on sintered moldings |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8948-65 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ColorRx® PCPT-1000NB | LTL Color Compounders, Inc. | PC+PET | ColorRx® |
| Generic HDPE, MMW | Generic | HDPE, MMW | Generic |
| Hyflon® MFA® 1041 | Solvay Specialty Polymers | Perfluoropolymer | Hyflon® MFA® |
| Polifil® PP T-30 | The Plastics Group | PP Homopolymer | Polifil® PP |