Electroblend® HIPS-4900
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | Electroblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zOogSe_Electroblend-HIPS-4900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Electroblend® HIPS-4900 is an antistatic high impact polystyrenen compound. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.00 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 28.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 73 | % | ASTM D638 |
| Flexural Modulus | 2520 | MPa | ASTM D790 |
| Flexural Strength | 44.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.00 mm) | 80.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 to 1.0E+10 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 200 to 205 | °C | |
| Middle Temperature | 205 to 210 | °C | |
| Front Temperature | 210 to 220 | °C | |
| Nozzle Temperature | 220 to 230 | °C | |
| Processing (Melt) Temp | 200 to 230 | °C | |
| Mold Temperature | 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DynaMix™ PA625-60 | Polymer Dynamix | Nylon 6 | DynaMix™ |
| LUVOCOM® 19-7278 | Lehmann & Voss & Co. | Nylon 46 | LUVOCOM® |
| KMI PP KM-699IB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |
| LNP™ LUBRICOMP™ OL004 compound | SABIC Innovative Plastics | PPS, Linear | LNP™ LUBRICOMP™ |
| Kepital® ET-20S | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |