LUBEMID A26 FR V0 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LUBEN PLAST srl |
| Trademark: | LUBEMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zOcWM0_LUBEMID-A26-FR-V0-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on PA6,6 first choice natural colour. Flame retarded. UL 94 V0 classified. With halogens. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 to 1.36 | g/cm³ | ISO 1183/A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 to 2700 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/5 | ||
| Yield | 45.0 to 55.0 | MPa | |
| Break | 35.0 to 45.0 | MPa | |
| Tensile Strain | ISO 527-2/1A/5 | ||
| Yield | 2.0 to 3.0 | % | |
| Break | 3.0 to 5.0 | % | |
| Flexural Modulus 1 | 1500 to 2000 | MPa | ISO 178 |
| Flexural Stress 2 | 40.0 to 50.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 to 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 to 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 25 to 35 | J/m | ASTM D256A |
| 23°C 3 | 40 to 50 | kJ/m² | ASTM D256 |
| 23°C | 2.0 to 3.0 | kJ/m² | ISO 180/A |
| 23°C 4 | 2.5 to 3.5 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 35 to 45 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 210 to 220 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 220 to 230 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 70.0 to 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 235 to 245 | °C | ISO 306/A120 |
| -- | 225 to 235 | °C | ISO 306/B120 |
| Melting Temperature | 250 to 265 | °C | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| 4 . | Notch A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| megol® HT SV/P 60 | API SpA | SEBS | megol® |
| SUMILITE® PL-1766 | Sumitomo Bakelite Co., Ltd. | Phenolic | SUMILITE® |
| VALOX™ EH7020 resin | SABIC Innovative Plastics | PBT | VALOX™ |
| Chemical Resources PP 2000W | Chemical Resources, Inc. | PP Homopolymer | Chemical Resources |
| CP PRYME® Polypropylene PPH100-.7FM | Chase Plastics Services Inc. | PP Homopolymer | CP PRYME® Polypropylene |