Bayflex® 970
| Category: | PUR-MDI , Polyurethane (MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Bayflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zOc7zr_Bayflex-970.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bayflex 970 is a fully compounded polyether-based polyurethane system consisting of two liquid components which can be water-blown. Component A is a modified diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol system. The Bayflex 970 system is used in the manufacture of microcellular polyurethane shoe soles. Soles prepared from these components combine light weight, comfort, and durability. Processibility and dynamic flexural properties are excellent over a wide range of densities. The combination of excellent physical properties and ease of processing has made the Bayflex 970 system a prime soling material for sandals, fashion and casual shoes. As with any product, use of the Bayflex 970 system in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.500 | g/cm³ | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 52 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 70.0 | mg | ASTM D3489 |
| Ross Flex 1 | ASTM D1052 | ||
| -29°C, 6.35 mm | > 5.0E+4 | Cycles | ASTM D1052 |
| 23°C, 6.35 mm | > 1.0E+5 | Cycles | ASTM D1052 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oil Resistance - Volume Swell | vol% | ASTM D5694 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 3.10 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 400 | % | ASTM D412 |
| Tear Strength | |||
| -- 2 | 14.0 | kN/m | ASTM D624 |
| -- 3 | 4.38 | kN/m | Internal method |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 63 | ||
| Component B | Mixing ratio by weight: 100 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Part A Type: Isocyanate Appearance: Light yellow to yellow liquid Specific Gravity @ 25°C: 1.19 Viscosity @25°C: 400 mPa*s Flash Point PMCC: >93°C Bulk Density @ 20°C: 9.93 lb/gal NCO: 18.9 wt% Part B Type: Polyol Appearance: White liquid Specific Gravity @ 25°C: 1.04 Viscosity @25°C: 1100 mPa*s Flash Point PMCC: 138°C Bulk Density @ 25°C: 8.68 lb/gal Water: 0.45 wt% Hydroxyl Number: 133 Material Temperature: 28°CMold Temperature: 49°CDemold Time: 3.5 minLinear Shrinkage@ 0.10 g/cm: <1.0%Hand Mix Reactivity @ 25°C Cream Time: 12 to 16 sec Tack Free: 30 to 40 sec Pull Time: 45 to 60 sec Free-Rise Density: 12.6 to 14.9 lb/ft³ |
| Note Message | |
|---|---|
| 1 . | 0% Cut Growth |
| 2 . | Die C |
| 3 . | Block |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Techsil RTV2420 | Techsil Limited | Silicone | Techsil |
| SLOVASTER® B2 BT | Plastcom | PBT | SLOVASTER® |
| Durez® 7347A | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| HiFill® PA4/6 HS LBK | Techmer Engineered Solutions | Nylon 46 | HiFill® |
| Sylvin 8036-85 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |