Monprene® CP-19078
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Monprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zO1R3D_Monprene-CP-19078.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Monprene CP-19078 is a general purpose thermoplastic elastomer designed for a variety of consumer product applications requiring a soft, rubber-like feel. Monprene CP-19078 is a high hardness, low density grade that exhibits medium flow characteristics, suitable for injection molding and extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.938 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 second, injection molding | 80 | ASTM D2240 | |
| Shore A, 5 seconds, injection molding | 78 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Transverse flow : 100% strain 1 | 3.79 | MPa | ASTM D412 |
| Flow : 100% strain 2 | 6.48 | MPa | ASTM D412 |
| Transverse flow : 300% strain 3 | 4.14 | MPa | ASTM D412 |
| Flow : 300% strain 4 | 7.47 | MPa | ASTM D412 |
| Tensile Strength | ASTM D412 | ||
| Transverse flow : Fracture 5 | 9.22 | MPa | ASTM D412 |
| Flow : Fracture 6 | 7.65 | MPa | ASTM D412 |
| Tensile Elongation | ASTM D412 | ||
| Transverse flow : Fracture 7 | 2200 | % | ASTM D412 |
| Flow : Fracture 8 | 390 | % | ASTM D412 |
| Tear Strength 9 | ASTM D624 | ||
| Transverse flow | 50.3 | kN/m | ASTM D624 |
| Flow | 52.5 | kN/m | ASTM D624 |
| Compression Set 10 | ASTM D395B | ||
| 23°C, 22 hr | 26 | % | ASTM D395B |
| 70°C, 22 hr | 62 | % | ASTM D395B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 182 - 232 | °C | |
| Middle Temperature | 188 - 238 | °C | |
| Front Temperature | 193 - 243 | °C | |
| Nozzle Temperature | 199 - 249 | °C | |
| Processing (Melt) Temp | 199 - 249 | °C | |
| Mold Temperature | 35.0 - 48.9 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 182 - 232 | °C | |
| Cylinder Zone 2 Temp. | 188 - 238 | °C | |
| Cylinder Zone 3 Temp. | 193 - 243 | °C | |
| Cylinder Zone 5 Temp. | 199 - 249 | °C | |
| Die Temperature | 199 - 249 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | Mouth die C, 510mm/min |
| 3 . | 510 mm/min |
| 4 . | C mold, 510mm/min |
| 5 . | 510 mm/min |
| 6 . | C mold, 510mm/min |
| 7 . | 510 mm/min |
| 8 . | Mouth die C, 510mm/min |
| 9 . | C mold, 510mm/min |
| 10 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinelec CCB6825 | Teknor Apex Asia Pacific PTE. LTD. | PS (Specialty) | Sinelec |
| GAPEX® APP30GP08HB NATURAL | Ferro Corporation | PP Homopolymer | GAPEX® |
| ENVIRON® ENV39-NC510 | ENVIROPLAS®, Inc. | PC+PBT | ENVIRON® |
| LNP™ STAT-KON™ PD000 compound | SABIC Innovative Plastics Europe | Nylon 6 | LNP™ STAT-KON™ |
| Durethan® B 35 F 000000 | LANXESS Corporation | Nylon 6 | Durethan® |