Braskem PP H 203
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Braskem |
| Trademark: | Braskem PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zNwy8g_Braskem-PP-H-203.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
H 203 is a high melt flow rate additivated homopolymer used for general purposes. This product exhibits excellent processability and good stiffness/impact strength balance. It also features low taste/odor transfer. Applications: Injection of electric portables and household appliances; Injected chest drawers and closets. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale, Injection Molded | 97 | ASTM D785 | |
| R-Scale | 97 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Injection Molded) | 35.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Yield, Injection Molded) | 11 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 1% Secant : Injection Molded | 1100 | MPa | ASTM D790 |
| Injection Molded | 1300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, Injection Molded | 30 | J/m | ASTM D256 |
| 23°C, Injection Molded | 2.9 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, Injection Molded | 96.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 96.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, Injection Molded | 56.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 56.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 152 | °C | ISO 306/A, ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miflon® 2223B | Jiangsu Meilan Chemical Co., Ltd. | PTFE | Miflon® |
| Baoding 6126S | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU, Unspecified | Baoding |
| Axplas® MEP52 0000 | Axion Polymers | TP, Unspecified | Axplas® |
| Karina CLEAR PVC COPOUND -E 65/207-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 2990-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |