| LOXIM 315 01 V0 is a Polyamide 6 (Nylon 6) product filled with 15% glass fiber. It is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D1299 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 80.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 to 5.0 | % | ASTM D638 |
| Flexural Modulus | 5000 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 190 | °C | ASTM D648B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1009 | RTP Company | PBT | RTP |
| Witcobond® W-242 | Chemtura | PUR-Ester | Witcobond® |
| EPIMIX PBT IMP NC B801 | EPSAN Plastik SAN. ve TiC. A.S. | PBT | EPIMIX |
| Karina WHITE PVC COMPOUND -E 753D10/ 11-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sumiliteresin® ECP-294 | SBHPP | Epoxy | Sumiliteresin® |