VITAMIDE® BF23WT6618
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zMg0dt_VITAMIDE-BF23WT6618.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VITAMIDE® BF23WT6618 is a Polyamide 6 (Nylon 6) product. It is available in Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption | |||
| 24 hr | 1.0 | % | ASTM D570 |
| 23°C, 24 hr | 1.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Break | 80.0 | MPa | ISO 527-2 |
| -- | 80.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 3200 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 95.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 90 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength | 3.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 200 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 218 | °C | ISO 1218, ASTM D2117 |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257, IEC 60093 |
| Dielectric Strength | 37 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | |||
| Solution A | 600 | V | IEC 60112 |
| -- | 600 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.750 mm | 850 | °C | |
| 1.50 mm | 850 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 775 | °C | |
| 1.50 mm | 775 | °C | |
| Oxygen Index | > 30 | % | ASTM D2863, ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E660MZAA | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Siloxane Masterbatch MB50-008 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| Next Nylon 66 Prime Series PXH-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Flontech® FT-GL15-GR5-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Mediprene® 500702M | ELASTO | SEBS | Mediprene® |