Order Products : sales@su-jiao.com
Generic TP, Unspecified
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zMLdne_Generic-TP-Unspecified.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic TP, Unspecified This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.811 - 1.60 | g/cm³ | ASTM D792 |
| 23°C | 0.954 - 1.40 | g/cm³ | ISO 1183 |
| -- | 1.09 - 1.22 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.52 - 0.72 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) | |||
| 300°C/1.2 kg | 0.50 - 45 | g/10 min | ASTM D1238 |
| 150°C/21.6 kg | 4.0 - 8.9 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (23°C) | 0.050 - 0.42 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.010 - 0.14 | % | ASTM D570 |
| Environmental Stress-Cracking Resistance (23°C) | 504 - 720 | hr | ASTM D1693 |
| Mooney Viscosity | 40 - 45 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 34 - 126 | ASTM D785 | |
| Durometer Hardness | |||
| 23°C | 45 - 96 | ASTM D2240 | |
| 23°C | 39 - 88 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 0.755 - 3210 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield, 23°C | 26.8 - 74.0 | MPa | ASTM D638 |
| Yield, 23°C | 0.0276 - 16.4 | MPa | ISO 527-2 |
| Fracture, 23°C | 2.20 - 60.3 | MPa | ASTM D638 |
| 23°C | 0.862 - 57.6 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 8.2 - 38 | % | ASTM D638 |
| Fracture, 23°C | 0.14 - 30 | % | ASTM D638 |
| Fracture, 23°C | 150 - 1100 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 50.3 - 3490 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| 23°C | 2.05 - 126 | MPa | ASTM D790 |
| Yield, 23°C | 17.9 - 123 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 97.0 - 175 | MPa | ASTM D695 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 10.5 - 15.0 | MPa | ISO 37 |
| Tensile Elongation (Break, 23°C) | 150 - 200 | % | ISO 37 |
| Tear Strength (23°C) | 5.00 - 116 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 9.6 - 130 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 29 - 500 | J/m | ASTM D256 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength (23°C) | -21 - 0.50 | % | ISO 1817 |
| Change in Tensile Strain at Break (23°C) | -15 - -4.1 | % | ISO 1817 |
| Change in Volume (23°C) | 0.88 - 20 | % | ISO 1817 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 49.9 - 133 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 36.7 - 164 | °C | ASTM D648 |
| Brittleness Temperature | -40.2 - -39.4 | °C | ASTM D746 |
| Glass Transition Temperature | |||
| -- | -54.0 - 104 | °C | ASTM E1356 |
| -- | -40.0 - 171 | °C | DSC |
| Melting Temperature | 203 - 263 | °C | |
| CLTE - Flow | |||
| -- | 2.9E-5 - 2.1E-4 | cm/cm/°C | ASTM D696 |
| -- | 3.1E-5 - 1.5E-4 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity (23°C) | 0.21 - 0.22 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 - 1.3E+14 | ohms | ASTM D257 |
| Volume Resistivity | |||
| 23°C | 10 - 2.2E+15 | ohms·cm | ASTM D257 |
| 23°C | 6.0 - 18 | ohms·cm | ASTM D991 |
| Dielectric Strength (23°C) | 13 - 16 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 1.66 - 4.82 | ASTM D150 | |
| Dissipation Factor (23°C) | 3.0E-4 - 0.22 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | |||
| -- | 29 - 44 | % | ASTM D2863 |
| -- | 30 - 45 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.502 - 1.585 | ASTM D542 | |
| Transmittance | 90.0 - 92.0 | % | ASTM D1003 |
| Haze | 1.0 - 4.5 | % | ASTM D1003 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Mix Viscosity | 72.0 - 5060 | cP | ASTM D2393 |
| Demold Time | 2.5 - 450 | min | |
| Post Cure Time | 8.0 | hr |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.8 - 80.3 | °C | |
| Drying Time | 3.0 - 3.1 | hr | |
| Rear Temperature | 179 - 288 | °C | |
| Middle Temperature | 186 - 299 | °C | |
| Front Temperature | 194 - 308 | °C | |
| Nozzle Temperature | 190 - 311 | °C | |
| Processing (Melt) Temp | 197 - 310 | °C | |
| Mold Temperature | 23.9 - 136 | °C | |
| Back Pressure | 0.517 - 0.862 | MPa | |
| Screw Speed | 55 - 61 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic TP, UnspecifiedThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 66.1 | °C | |
| Drying Time | 2.0 - 6.0 | hr | |
| Cylinder Zone 1 Temp. | 130 - 181 | °C | |
| Cylinder Zone 2 Temp. | 138 - 161 | °C | |
| Cylinder Zone 3 Temp. | 145 - 167 | °C | |
| Cylinder Zone 4 Temp. | 150 - 182 | °C | |
| Cylinder Zone 5 Temp. | 158 - 173 | °C | |
| Melt Temperature | 127 - 227 | °C | |
| Die Temperature | 157 - 206 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic TP, UnspecifiedThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Multi-Flam™ 0801 | Multibase, A Dow Corning Company | LDPE | Multi-Flam™ |
| Cellophane™ 350P23 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Clariant Nylon 6/6 PA-113G33 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Daelim Po1y® LH210 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| EcoPaXX® Q150-D | DSM Engineering Plastics | Nylon 410 | EcoPaXX® |