Diaterm® B26 GF35
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | DTR S.r.l. (Develop Thermoplastic Resins) |
| Trademark: | Diaterm® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zLoKWE_Diaterm-B26-GF35.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Diaterm®B26 GF35 is a polyamide 66 (nylon 66) material, which contains a 35% glass fiber reinforced material. This product is available in Europe,. Diaterm®The main characteristics of B26 GF35 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 170 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 9900 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 90 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 255 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 245 | °C | ASTM D648 |
| Vicat Softening Temperature | 255 | °C | ASTM D1525 1 |
| Melting Temperature | 260 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| Water Absorption, DIN 53714, 23°C, 50% RH: 1.9%Burning Rate, DIN 75200: <100mm/min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr |
| Note Message | |
|---|---|
| 1 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reon 67-01 | Reliance Industries Limited | PVC Homopolymer | Reon |
| Taitacell EPS 351S | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| UBE Polyethylene F022SE | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| Axiall PVC 8941 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Devcon Underwater Repair Putty (UW) | Devcon | Epoxy | Devcon |