Shinkolite MR
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Mitsubishi Rayon Co., Ltd. |
| Trademark: | Shinkolite |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zLo3PX_ShinkoliteMR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Shinkolite MR is a polymethyl methacrylate-acrylic material,. This product is available in North America, Europe or Asia Pacific,. The main characteristics of Shinkolite MR are: odorless/tasteless tract. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption | |||
| 24 hr | 0.30 | % | ASTM D570 |
| 23°C, 24 hr | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | 100 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ASTM D638, ISO 527-2/1B/1 |
| Tensile Strength (Break) | 64.0 | MPa | ASTM D638, ISO 527-2/1B/5 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638, ISO 527-2/1B/5 |
| Flexural Modulus | 3200 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 91.0 | MPa | ISO 178 |
| Fracture | 91.0 | MPa | ASTM D790 |
| Compressive Modulus | 3200 | MPa | ASTM D695, ISO 604 |
| Compressive Strength | 120 | MPa | ASTM D695, ISO 604 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 100 | °C | ASTM D648, ISO 75-2/A |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696, ISO 11359-2 |
| Specific Heat | 1500 | J/kg/°C | |
| Thermal Conductivity | 0.21 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 1 | > 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 2 | 20 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 4.00 | ASTM D150 | |
| 1 kHz | 4.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 0.060 | ASTM D150 | |
| 1 kHz | 0.040 | ASTM D150 | |
| 1 MHz | 0.020 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | |||
| -- | 33 | mm/min | ISO 1210 |
| -- | 33 | mm/min | ASTM D635 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | |||
| -- | 1.520 | ASTM D542 | |
| -- 3 | 1.520 | ISO 489 | |
| Transmittance | |||
| Total | 93.0 | % | ASTM D1003 |
| Total | 93.0 | % | ISO 13468-1 |
| Haze | |||
| -- | 0.50 | % | ASTM D1003 |
| -- | 0.50 | % | ISO 14782 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Soluble Matter Loss - after immersion | 0.0 | % |
| Note Message | |
|---|---|
| 1 . | 28°C, 75%RH |
| 2 . | Method A (short time) |
| 3 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Yuyao PP TL303 | Yuyao Tenglong Plastics Co., Ltd. | PP, Unspecified | Yuyao PP |
| ESPRENE EPDM 600F | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |
| KOPLA PA66 KDX1067 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| Petrotene® PP A3 T35 PRTA011 PH355 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |
| Polifor® C 30 TE/40 BIANCO Y1 | SO.F.TER. SPA | PP Copolymer | Polifor® |