SABIC® PP RA1E10h
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zLABQk_SABIC-PP-RA1E10h.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This random copolymer has a high molecular weight and therefore mainly used for extrusion. It is typically used in pipe & sheet extrusion. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.895 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 | |
| Shore Hardness (Shore D) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1000 | MPa | ASTM D638 |
| -- | 950 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 28.0 | MPa | ASTM D638 |
| Yield | 29.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 13 | % | ASTM D638 |
| Yield | 12 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | > 60 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D256A |
| 23°C | 14 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 128 | °C | ASTM D1525, ISO 306/A120 4 4 |
| -- | 67.0 | °C | ASTM D1525, ISO 306/B120 5 5 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | Rate B (120°C/h), Loading 1 (10 N) |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® QE548AE | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| SCHULAMID® 66 MW 30 FR 4 K2031 | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Sinvicomp SIZ4508A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| POLYCHIM B 10 TB | POLYCHIM INDUSTRIES | PP Homopolymer | POLYCHIM |
| ESTOPLAST EP 4030WW20 | Ester Industries Ltd. | PBT | ESTOPLAST EP |