Diamond ASA S246
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Diamond ASA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zKyeG9_Diamond-ASA-S246.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Diamond ASA S246 is an Acrylonitrile Styrene Acrylate (ASA) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(220°C/10.0 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Tangent 2(23°C, Injection Molded) | 2570 | MPa | ASTM D638 |
| Tensile Strength 3(Yield, 23°C, Injection Molded) | 45.9 | MPa | ASTM D638 |
| Tensile Elongation 4(Yield, 23°C, Injection Molded) | 2.9 | % | ASTM D638 |
| Flexural Modulus - Tangent 5(3.18 mm, 50.8 mm Span) | 2500 | MPa | ASTM D790 |
| Flexural Strength 6(Yield, 23°C, 3.18 mm, Injection Molded, 50.8 mm Span) | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm, Injection Molded) | 78.9 | °C | ASTM D648 |
| Vicat Softening Temperature | 106 | °C | ASTM D1525 7 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 70 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 230 to 249 | °C | |
| Middle Temperature | 232 to 260 | °C | |
| Front Temperature | 235 to 260 | °C | |
| Nozzle Temperature | 220 to 260 | °C | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 65.6 to 82.2 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.517 to 1.03 | MPa |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | Type I, 51 mm/min |
| 5 . | Method I (3 point load), 1.3 mm/min |
| 6 . | Method I (3 point load), 1.3 mm/min |
| 7 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fluoroplex CG 25 - GML | UNIFLON | PTFE | Fluoroplex |
| Electrafil® ABS 03010 | Techmer Engineered Solutions | ABS | Electrafil® |
| Karina WHITE PVC COMPOUND 800-10/93-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ICORENE® 1506 | A. Schulman Europe | XLPE | ICORENE® |
| Kepital® F10-02 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |