Pro-fax EP390P
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Pro-fax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zKhTZG_Pro-fax-EP390P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pro-fax EP390P high impact polypropylene copolymer is available in pellet form. This resin has minimal stabilization, which allows wide design latitude for the compounder. Additional stabilization is required to protect the resin during melt processing and throughout its useful life. For regulatory compliance information see Pro-fax EP390P Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792B |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 6.0 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 2 | 1040 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | No Break | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 82.0 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 801 GB 10 | RTP Company | Acetal (POM) Copolymer | RTP |
| Qenos PP PPW 1762 | Qenos Pty Ltd | PP Copolymer | Qenos PP |
| Keltan® 7550 | LANXESS Buna GmbH | EPDM | Keltan® |
| Kumho ABS HU600DS | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |
| INNOPOL® PP CS 2-9524 | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |