Kepital® F20-52
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zIgHvt_Kepital-F20-52.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A medium viscosity grade, natural color, for weather resistance purpose. It has stability on UV light, and so good at out-door use. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 2.0 | % | ASTM D955 |
| 3.00 mm | 2.0 | % | |
| Water Absorption (Equilibrium, 23°C, 60%) | 0.22 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 57.0 | MPa | ASTM D638 |
| Yield, 23°C | 63.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 55 | % | ASTM D638 |
| Nominal Tensile Strain at Break | 35 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2310 | MPa | ASTM D790 |
| 23°C | 2350 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 80.4 | MPa | ASTM D790 |
| 23°C | 83.0 | MPa | ISO 178 |
| Shear Strength | 54.9 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (3.20 mm) | 59 | J/m | ASTM D256 |
| Tensile Impact Strength (1.60 mm) | 107 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 158 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 110 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 92.0 | °C | ISO 75-2/A |
| Melting Temperature | 165 | °C | |
| CLTE - Flow | 1.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+16 | ohms | ASTM D257 |
| -- | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | |||
| -- | 1.0E+14 | ohms·cm | ASTM D257 |
| -- | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength | 19 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.70 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 7.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APICAL 300AV | Kaneka Corporation | PI, TS | APICAL |
| Favorite MDLLN | Favorite Plastics | PE, Unspecified | Favorite |
| Karina CLEAR PVC COMPOUND 74/203-D-IS-SI (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYblend PC/ABS 85VB | Polykemi AB | PC+ABS | POLYblend |
| Polifor® 12 TR/20 UV NATURALE | SO.F.TER. SPA | PP Homopolymer | Polifor® |