DOW™ LDPE 310E

Category:	LDPE , Low Density Polyethylene Resin
Manufacturer:	The Dow Chemical Company
Trademark:	DOW™ LDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	zIMTbw_DOW-LDPE-310E.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

DOW LDPE 310E is a fractional melt index low density polyethylene resin. DOW LDPE 310E has been specially designed for superior processability on blown film lines leading to significant output improvements. The resin offers additionally excellent draw down. It can be used pure or in blends with LLDPE resins.

Applications:

lamination film, shrink film, and stretch film

Main Characteristics:

Excellent processability and draw down

Good physical properties in blends with LLDPE

Can be readily extruded using conventional blown film techniques at melt temperatures between 160 and 195°C

Complies with:

U.S. FDA 21 CFR 177.1520 ( c )2.2

EU, No 10/2011

U.S. FDA-DMF

Canadian HPFB No Objection

Consult the regulations for complete details.

Slip Additive: 0 ppm
Antiblock Additive: 0 ppm

General Information
Agency Ratings	DMF not rated FDA 21 CFR 177.1520(c) 2.2 HPFB (Canada) No Objection Europe No 10/2011
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.923	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.75	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction	0.50 - 0.70		ASTM D1894

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	50	µm
Film Puncture Energy (50 µm)	1.80	J	Internal method
Film Puncture Force (50 µm)	50.0	N	Internal method
Film Puncture Resistance (50 µm)	4.00	J/cm³	Internal method
secant modulus			ASTM D882
2% secant, MD : 50 µm, blown film	175	MPa	ASTM D882
2% secant, TD : 50 µm, blown film	185	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Yield, 50 µm, blown film	11.0	MPa	ASTM D882
TD : Yield, 50 µm, blown film	11.0	MPa	ASTM D882
MD : Broken, 50 µm, blown film	25.0	MPa	ASTM D882
TD : Broken, 50 µm, blown film	23.0	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Broken, 50 µm, blown film	390	%	ASTM D882
TD : Broken, 50 µm, blown film	570	%	ASTM D882
Dart Drop Impact (50 µm, Blown Film)	170	g	ASTM D1709A
Elmendorf Tear Strength ¹			ASTM D1922
MD : 50 µm, blown film	350	g	ASTM D1922
TD : 50 µm, blown film	260	g	ASTM D1922

Optical	Nominal Value	Unit	Test Method
Gloss (45°, 50.0 µm, Blown Film)	58		ASTM D2457
Haze (50.0 µm, Blown Film)	9.2	%	ASTM D1003

Extrusion	Nominal Value	Unit
Melt Temperature	160 - 195	°C

Extrusion instructions
吹塑薄膜的制造条件：螺杆类型：通用输出：25 kg/h 模具直径：150 mm。放大比：2.5 螺杆速度：77 rpm

Note Message
1 .	Method B

Resin Grade	Manufacturer	Category	Trademark
RheTech Polypropylene HP512-00	RheTech, Inc.	PP Copolymer	RheTech Polypropylene
Sylvin 8320-75 Black	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
TES J-1200/20/VO/Natl	Techmer Engineered Solutions	ABS	TES
DINALON® A1X25 G30V0	Grupo Repol	Nylon 66	DINALON®
Osterlene® LLSH0917A	Osterman & Company	LLDPE	Osterlene®