LNP™ LUBRICOMP™ 5CL23 compound
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zI8gVc_LNP-LUBRICOMP-5CL23-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP 5CL23 is a compound based on PVDF resin containing 15% Carbon Fiber, 10% PTFE. Added features include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound FP-VCL-4023 Product reorder name: 5CL23 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.84 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.50 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.030 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 15800 | MPa | ASTM D638 |
| -- | 14500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 84.0 | MPa | ASTM D638 |
| Break | 77.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 0.80 | % | ASTM D638 |
| Break | 0.70 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 12500 | MPa | ASTM D790 |
| -- 5 | 11900 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 100 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 108 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.53 | ||
| vs. Itself - Static | 0.44 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.00 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 5.00 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 55 | J/m | ASTM D256 |
| 23°C 7 | 5.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 200 | J/m | ASTM D4812 |
| 23°C 8 | 13 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 13.5 | J | ASTM D3763 |
| -- | 3.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 168 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 166 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 164 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 158 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.1E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.4E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 210 to 225 | °C | |
| Front Temperature | 225 to 245 | °C | |
| Processing (Melt) Temp | 215 to 230 | °C | |
| Mold Temperature | 65.0 to 90.0 | °C | |
| Back Pressure | 0.170 to 0.340 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ PA666G33HS1L-BK10 | Pier One Polymers, Inc. | Nylon 66/6 | MAXAMID™ |
| LNP™ THERMOCOMP™ KX97390 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ THERMOCOMP™ |
| MAJ'ECO DP290MBSE | AD majoris | PE, Unspecified | MAJ'ECO |
| Osterlene® PPR02CLNX | Osterman & Company | PP Random Copolymer | Osterlene® |
| Durethan® BKV 30 H3.0 000000 | LANXESS GmbH | Nylon 6 | Durethan® |