Optimum® 800
| Category: | Copolyester , Copolyester |
| Manufacturer: | RAUH Polymers, Inc. |
| Trademark: | Optimum® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zI0mFq_Optimum-800.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Optimum® 800 is a Copolyester product. It can be processed by injection molding and is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 40 to 50 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 53.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 150 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 910 | J/m | ASTM D256 |
| Instrumented Dart Impact | 36.2 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.18 mm) | 125 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 to 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 260 to 266 | °C | |
| Middle Temperature | 266 to 271 | °C | |
| Front Temperature | 266 to 271 | °C | |
| Nozzle Temperature | 274 to 277 | °C | |
| Processing (Melt) Temp | 232 to 266 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Injection Pressure | 55.2 to 68.9 | MPa | |
| Injection Rate | Moderate | ||
| Holding Pressure | 41.4 to 55.2 | MPa | |
| Back Pressure | 0.00 to 2.76 | MPa |
| Note Message | |
|---|---|
| 1 . | Type I |
| 2 . | Type I |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UmaPET HC | Ester Industries Ltd. | PET | UmaPET |
| AFFINITY™ PL 1880G | The Dow Chemical Company | POP | AFFINITY™ |
| Grivory® GV-4 FWA black 9225 | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| INNOPOL® PP CS 2-5840 GB | Inno-Comp Ltd. | PP Impact Copolymer | INNOPOL® PP |
| Karina IVORY PVC COMPOUND -E 650D35/ 1-C | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |