ELITE™ 5811
| Category: | EPE , Enhanced Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ELITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zGxqqN_ELITE-5811.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ELITE 5811 is an extrusion coating resin. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.919 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 21.2 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 720 | % | ISO 527-2 |
| Flexural Modulus | 307 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 527-3 | ||
| MD : Yield | 19.3 | MPa | |
| TD : Yield | 16.2 | MPa | |
| Tensile Elongation 2 | ISO 527-3 | ||
| MD : Break | 540 | % | |
| TD : Break | 610 | % | |
| Elmendorf Tear Strength 3 | ISO 6383-2 | ||
| MD | 2.4 | N | |
| TD | 3.8 | N | |
| Seal Initiation Temperature 4 | 98.0 | °C | Internal Method |
| Water Vapor Transmission 5 | 18 | g/m²/24 hr | ASTM E96 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 102 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 124 | °C | Internal Method |
| Extrusion | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Temperature | 260 to 320 | °C | |
| Draw Down - From 15g/m² at 100 m/min 6 | 250 | m/min | Internal Method |
| Minimum Coating Weight - Calculated 7 | 6.0 | g/m² | Internal Method |
| Neck-in - 25g/m² at 100 m/min 8(290°C) | 84.0 | mm | Internal Method |
| Note Message | |
|---|---|
| 1 . | 25g/m² coating onto paper substrate and/or coating web at 250 mm air gap and -15 nip off-set. |
| 2 . | 25g/m² coating onto paper substrate and/or coating web at 250 mm air gap and -15 nip off-set. |
| 3 . | 25g/m² coating onto paper substrate and/or coating web at 250 mm air gap and -15 nip off-set. |
| 4 . | - 25g/m² coating onto paper substrate and/or coating web at 250 mm air gap and -15 nip off-set.- Temperatures at which 3 N/15mm heat seal strength is achieved.- Heat Seal Strengths measured at 0.5sec sealing time, 0.5N/mm² pressure, 5mm seal bar, cross head speed (150 mm/sec).- Kraft paper substrate |
| 5 . | 25g/m² coating onto paper substrate and/or coating web at 250 mm air gap and -15 nip off-set. |
| 6 . | 25g/m² coating onto paper substrate and/or coating web at 250 mm air gap and -15 nip off-set. |
| 7 . | 25g/m² coating onto paper substrate and/or coating web at 250 mm air gap and -15 nip off-set. |
| 8 . | 25g/m² coating onto paper substrate and/or coating web at 250 mm air gap and -15 nip off-set. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® VDC 300-40 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PVDC | TEKNIFLEX® |
| Sylvin 2990-50 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NEFTEKHIM PP 4254N | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Hanwha Total PP SB52S | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Hifax RTA3263/2 | LyondellBasell Industries | TPO (POE) | Hifax |