PRL PEI-G20
| Category: | PEI , Polyether Imide |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zGtpxu_PRL-PEI-G20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PEI-G20 is a Polyether Imide (PEI) product filled with 20% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 5.0 to 22 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.19 | % | |
| Equilibrium, 23°C | 1.1 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.18 mm) | 6830 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 138 | MPa | |
| Break, 3.18 mm | 138 | MPa | |
| Tensile Elongation (Break, 3.18 mm) | 4.0 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 6830 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 221 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.18 mm) | 480 | J/m | ASTM D4812 |
| Reverse Notch Izod Impact (23°C, 3.18 mm) | 450 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 210 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 207 | °C | |
| Vicat Softening Temperature | 221 | °C | ASTM D1525 1 |
| CLTE - Flow (-20 to 150°C) | 2.5E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | UL 746 | ||
| 1.50 mm | 105 | °C | |
| 3.00 mm | 105 | °C | |
| RTI Imp | UL 746 | ||
| 1.50 mm | 105 | °C | |
| 3.00 mm | 105 | °C | |
| RTI Str | UL 746 | ||
| 1.50 mm | 105 | °C | |
| 3.00 mm | 105 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 7.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.59 mm, in Oil) | 26 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.50 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 1.5E-3 | ||
| 2.00 GHz | 4.9E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, ALL | V-0 | ||
| 3.00 mm, ALL | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 143 to 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Rear Temperature | 332 to 399 | °C | |
| Middle Temperature | 338 to 399 | °C | |
| Front Temperature | 343 to 399 | °C | |
| Processing (Melt) Temp | 338 to 399 | °C | |
| Mold Temperature | 107 to 177 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M3500CA (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| TEKAMID™ TA210L | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| CompaMid® PA 6.6 GF 10 M 20 | DimeLika Plast GmbH | Nylon 66 | CompaMid® |
| EZPrene 9070A | ENPLAST Americas, a Ravago Group Company | TPV | EZPrene |
| Sylvin 9077-70C LMW Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |