TECHNYL® A 30H1 V30 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zGiBHB_TECHNYL-A-30H1-V30-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® A 30H1 V30 Natural is a brominated flame retardant polyamide 66, reinforced with 30% of glass fibre, for injection moulding. This product is available in natural color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.57 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.95 | -- | % | |
| Flow | 0.60 | -- | % | |
| Water Absorption (Saturation, 23°C) | 0.80 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.630 | -- | Internal Method |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Fire and Smoke F Index | I3/F3 | -- | NF F16-101 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 7000 | MPa | ISO 527-2/1A |
| Tensile Strength | ||||
| Break | 140 | -- | MPa | ASTM D638 |
| Break | 130 | 95.0 | MPa | ISO 527-2/1A |
| Tensile Elongation | ||||
| Break | 2.5 | -- | % | ASTM D638 |
| Break | 2.2 | 3.5 | % | ISO 527-2/1A |
| Flexural Modulus | ||||
| -- | 9500 | -- | MPa | ASTM D790 |
| -- | 9500 | 7000 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 200 | -- | MPa | ASTM D790 |
| -- | 200 | 170 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.5 | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 42 | 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| 23°C | 120 | -- | J/m | ASTM D256 |
| 23°C | 10 | 13 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 1.8 MPa, Unannealed | 227 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 226 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 42 | 40 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.30 | 3.60 | IEC 60250 | |
| Dissipation Factor | 0.010 | 0.050 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 450 | 600 | V | |
| Solution B | 400 | 500 | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | V-0 | -- | ||
| 1.60 mm | V-0 | -- | ||
| 3.20 mm | V-0 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 960 | -- | °C | |
| 1.60 mm | 960 | -- | °C | |
| 3.20 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.800 mm | 800 | -- | °C | |
| 1.60 mm | 825 | -- | °C | |
| Oxygen Index | 31 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 270 to 280 | °C | |
| Middle Temperature | 275 to 285 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 2805 MAS145 | Covestro - Polycarbonates | PC | Makrolon® |
| Hybrid S464 | Ravago Manufacturing Americas, LLC | PC+ABS | Hybrid |
| Plenco 07321 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |
| TechnoElast V A9000 I 2 sw | TechnoCompound GmbH | TPE | TechnoElast |
| 3M™ Dyneon™ PTFE Compound 310160003 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |