PRL PC-UV2-D(f1)-(color)-1

Category:	PC , Polycarbonate
Manufacturer:	Polymer Resources Ltd.
Trademark:	PRL
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	zGfkiC_PRL-PC-UV2-D-f1---color--1.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

PRL PC-UV2-D(f1)-(color)-1 is a Polycarbonate (PC) product. It can be processed by injection molding and is available in North America. Typical application: Outdoor Applications.

Characteristics include:

Flame Rated

RoHS Compliant

Good Mold Release

Good UV Resistance

Mold Release Agent

General Information
Additive	Mold Release UV Stabilizer
Features	Good Mold Release Good UV Resistance Medium Flow
RoHS Compliance	RoHS Compliant
UL File Number	E113219
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.20	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)	9.0 to 16	g/10 min	ASTM D1238
Molding Shrinkage - Flow (3.18 mm)	0.50 to 0.70	%	ASTM D955
Outdoor Suitability	f1		UL 746C

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness			ASTM D785
M-Scale	70
R-Scale	118

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
Yield, 3.18 mm	62.1	MPa
Break, 3.18 mm	68.9	MPa
Tensile Elongation			ASTM D638
Yield, 3.18 mm	6.5	%
Break, 3.18 mm	140	%
Flexural Modulus (3.18 mm)	2310	MPa	ASTM D790
Flexural Strength (3.18 mm)	95.8	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, 3.18 mm)	800	J/m	ASTM D256
Gardner Impact (3.18 mm)	> 36.2	J	ASTM D3029

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, Unannealed, 3.18 mm	135	°C
1.8 MPa, Unannealed, 3.18 mm	129	°C
Vicat Softening Temperature	152	°C	ASTM D1525 ¹
RTI Elec			UL 746
0.749 mm	80.0	°C
1.50 mm	120	°C
3.00 mm	120	°C
RTI Imp			UL 746
0.749 mm	80.0	°C
1.50 mm	105	°C
3.00 mm	110	°C
RTI Str			UL 746
0.749 mm	80.0	°C
1.50 mm	120	°C
3.00 mm	120	°C

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	1.0E+15	ohms·cm	ASTM D257
Dielectric Strength (0.749 mm)	12	kV/mm	ASTM D149
Arc Resistance (0.749 mm)	PLC 5		ASTM D495
Comparative Tracking Index (CTI) (0.749 mm)	PLC 3		UL 746
High Amp Arc Ignition (HAI)			UL 746
1.50 mm	PLC 0
3.00 mm	PLC 0
High Voltage Arc Tracking Rate (HVTR) (0.749 mm)	PLC 2		UL 746
Hot-wire Ignition (HWI)			UL 746
1.50 mm	PLC 2
3.00 mm	PLC 2

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
0.749 mm, ALL	V-2
1.50 mm, ALL	V-2
3.00 mm, ALL	V-2

Optical	Nominal Value	Unit	Test Method
Transmittance (2540 µm)	88.0	%	ASTM D1003
Haze (2540 µm)	1.0	%	ASTM D1003

Injection	Nominal Value	Unit
Drying Temperature	118 to 124	°C
Drying Time	3.0 to 4.0	hr
Drying Time, Maximum	8.0	hr
Rear Temperature	271 to 293	°C
Middle Temperature	282 to 304	°C
Front Temperature	293 to 316	°C
Processing (Melt) Temp	288 to 316	°C
Mold Temperature	71.1 to 93.3	°C

Note Message
1 .	Rate B (120°C/h), Loading 2 (50 N)

Resin Grade	Manufacturer	Category	Trademark
RTP 1300 MG 50	RTP Company	PPS	RTP
Sylvin 5143-88 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Edgetek™ PC-20GF/000 NC008	PolyOne Corporation	PC	Edgetek™
Huafon JF-S-PV8030	Huafon Group Co., Ltd.	PUR, Unspecified	Huafon
Delene 2070	Shanghai Lin Gen Rubber Materials Co., Ltd.	TPE	Delene