LNP VERTON MV006BS is a compound based on Polypropylene resin containing 30% Long Glass Fiber. Added features of this grade include: Heat Stabilized, Burst Pressure, Structural, Chemically Coupled. Also known as: LNP* VERTON* Compound MFX-7006 HS BP Product reorder name: MV006BS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.60 | % | |
| Across Flow : 24 hr | 0.50 to 0.80 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.030 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6930 | MPa | ASTM D638 |
| -- | 6340 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 104 | MPa | ASTM D638 |
| Yield | 96.0 | MPa | ISO 527-2/5 |
| Break 3 | 104 | MPa | ASTM D638 |
| Break | 87.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.4 | % | ASTM D638 |
| Yield | 2.3 | % | ISO 527-2/5 |
| Break 5 | 2.4 | % | ASTM D638 |
| Break | 2.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 5840 | MPa | ASTM D790 |
| -- 7 | 6.00 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 145 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 162 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 210 | J/m | ASTM D256 |
| 23°C 9 | 20 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 770 | J/m | ASTM D4812 |
| 23°C 10 | 53 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 12.8 | J | ASTM D3763 |
| -- | 6.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 163 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 162 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 155 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 155 | °C | ISO 75-2/Af |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 7.6E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 232 to 243 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 249 to 260 | °C | |
| Processing (Melt) Temp | 221 to 249 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT4802-690UVA | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Nivionplast® A R306G NATURALE | SO.F.TER. SPA | Nylon 66 | Nivionplast® A |
| For-Tec E OC8OAN (Series: AD/PAX/MR) | KRAIBURG TPE | TPE | For-Tec |
| Petrothene® NA952 | LyondellBasell Industries | LDPE | Petrothene® |
| Sylvin 5042N-105-NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |