Category:	ABS , Acrylonitrile Butadiene Styrene
Manufacturer:	pal plast GmbH
Trademark:	PALRAN®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	zGKhWs_PALRAN-R-S-20.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
PALRAN®R S 20 is an acrylonitrile butadiene styrene (ABS) product,. It can be processed by injection molding and is available in Europe. Features include: flame retardant/rated flame Impact resistance Heat resistance

General Information
Features	Impact resistance, good Electroplateable Good liquidity Heat resistance, medium
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.04	g/cm³	ISO 1183
Water Absorption (Saturation, 23°C)	0.25	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	2100	MPa	ISO 527-2/1A/1
Tensile Stress (Yield, 23°C)	37.5	MPa	ISO 527-2/1A/50
Tensile Strain (Yield, 23°C)	22	%	ISO 527-2/1A/50

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	18	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	No Break		ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	92.5	°C	ISO 306/B50

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	HB		UL 94

Additional Information
Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2000 to 2200 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 35 to 40 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 20 to 24 %Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 15 to 20 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 90 to 95 °CDensity, ISO 1183: 1.03 to 1.05 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.2 to 0.3 %

Additional Information

Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2000 to 2200 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 35 to 40 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 20 to 24 %Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 15 to 20 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 90 to 95 °CDensity, ISO 1183: 1.03 to 1.05 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.2 to 0.3 %

Resin Grade	Manufacturer	Category	Trademark
SABIC® PPcompound 20MBT	Saudi Basic Industries Corporation (SABIC)	PP, Unspecified	SABIC® PPcompound
Wanthane® WHT-2185	Wanhua Chemical Group Co., Ltd.	TPU-Capro	Wanthane®
Unichem 8705	Colorite Polymers	PVC, Unspecified	Unichem
LOFEX® A3110	Lotte Chemical Corporation	PET	LOFEX®
Durethan® DP AKV 30 FN00 DUS013 000000	LANXESS GmbH	Nylon 66	Durethan®