Talcoprene® OC3030 CM GRIGIO313
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Talcoprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zG9oLt_Talcoprene-OC3030-CM-GRIGIO313.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Talcoprene® OC3030 CM GRIGIO313 is a Polypropylene material. It is available in Europe, Latin America, or North America for injection molding. Important attributes of Talcoprene® OC3030 CM GRIGIO313 are:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 1.1 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 27.0 | MPa | ASTM D638 |
| Flexural Modulus | 2800 | MPa | ASTM D790 |
| Flexural Strength | 48.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 28 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 66.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 92.0 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 190 | °C | |
| Middle Temperature | 210 | °C | |
| Front Temperature | 230 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 12N5006 | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| NEFTEKHIM PS 625 | Nizhnekamskneftekhim Inc. | PS (HIPS) | NEFTEKHIM PS |
| Nylene® 134 HSL | Custom Resins Group | Nylon 66 | Nylene® |
| MAJORIS CW337 - 7731 | AD majoris | PP Homopolymer | MAJORIS |
| TechnoElast A 8000 I 1 nat | TechnoCompound GmbH | TPE | TechnoElast |