Latistat 62-08
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latistat |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zG3fec_Latistat-62-08.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Dissipative product based on Polyamide 6 (PA 6). |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.2 to 1.4 | % | |
| Flow : 2.00 mm | 1.1 to 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 65.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 20 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 185 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 95.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+8 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Promyde® B242 HS | NUREL, S.A. | Nylon 6 | Promyde® |
| WELLAMID Nylon 6000 MRGV 20/10 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Nymax™ ND633 GF Black | PolyOne Corporation | Nylon 6 | Nymax™ |
| Kingfa JH710 G30 | Kingfa | PC Alloy | Kingfa |
| ULTEM™ HU1100 resin | SABIC Innovative Plastics | PEI | ULTEM™ |