LNP™ STAT-KON™ DE002 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zFdu0P_LNPSTATKONDE002compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* Stat-Kon* DE002 is a Polycarbonate containing Carbon Fiber. Also known as: LNP* STAT-KON* Compound DC-1002 Product reorder name: DE002 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.20 - 0.40 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.40 - 0.60 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.080 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.080 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11100 | MPa | ASTM D638 |
| -- | 10300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 97.0 | MPa | ASTM D638 |
| Fracture | 97.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 3 | 7.5 | % | ASTM D638 |
| Fracture | 7.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 7460 | MPa | ASTM D790 |
| -- 5 | 7440 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 149 | MPa | ISO 178 |
| Fracture, 50.0mm span 6 | 159 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 85 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 690 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 146 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 7 | 145 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 141 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 8 | 142 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -30 to 30°C | 2.6E-5 | cm/cm/°C | ASTM D696 |
| Lateral : -30 to 30°C | 5.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0 - 5.0 | ohms | ASTM D257 |
| Volume Resistivity | 4.0 - 6.0 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 mm |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 199 X 134954 A | RTP Company | PP, Unspecified | RTP |
| VYTEEN PC/ABS 8515 | Lavergne Group | PC+ABS | VYTEEN |
| Fusabond® C250 | DuPont Packaging & Industrial Polymers | EVA | Fusabond® |
| Generic PP Homopolymer - Glass Fiber, Long | Generic | PP Homopolymer | Generic |
| Lustran® ABS 248FC | Styrolution | ABS | Lustran® ABS |