WELLAMID Nylon 6600 CF 30 HWCP
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | CP-Polymer-Technik GmbH & Co. KG |
| Trademark: | WELLAMID Nylon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zElfsP_WELLAMID-Nylon-6600-CF-30-HWCP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WELLAMID Nylon 6600 CF 30 HWCP is a Polyamide 66 (Nylon 66) material filled with 30% carbon fiber. It is available in Europe. Important attributes of WELLAMID Nylon 6600 CF 30 HWCP are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.27 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 4.00 mm | 0.70 | -- | % | |
| Flow : 4.00 mm | 0.20 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.8 to 2.3 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 21000 | 16000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 205 | 145 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.6 | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus | 18500 | -- | MPa | DIN 52457 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | 18 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 42 | 78 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 230 | -- | °C | ISO 306/B50 |
| Melting Temperature | 255 | -- | °C | |
| CLTE - Flow (23 to 80°C) | 2.5E-5 | -- | cm/cm/°C | DIN 53752 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | < 10 | -- | ohms | IEC 60093 |
| Volume Resistivity | < 5.0 | -- | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 275 to 295 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 362 | RTP Company | PC | RTP |
| Sumitomo Phenolic FM 4005X4649 | Sumitomo Bakelite North America, Inc. | Phenolic | Sumitomo Phenolic |
| TOTAL Polyethylene EVA 1003 VN 4 | TOTAL Refining & Chemicals | EVA | TOTAL Polyethylene |
| FHR EPS 54-3654 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| ESTOPLAST SR 1500BL83 | Ester Industries Ltd. | ABS | ESTOPLAST SR |