LNP* LUBRICOMP* OCP36 is a compound based on Polyphenylene Sulfide resin containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this grade include: Internally Lubricated, Bearing Grade, Electrically Conductive. Also known as: LNP* LUBRICOMP* Compound O-BG Product reorder name: OCP36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.51 | g/cm³ | ASTM D792 |
| -- | 1.54 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.30 | % | |
| Across Flow : 24 hr | 0.40 to 0.60 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.022 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.029 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 26100 | MPa | ASTM D638 |
| -- | 24900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 165 | MPa | ASTM D638 |
| Break | 166 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 0.90 | % | ASTM D638 |
| Break | 0.90 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 21400 | MPa | ASTM D790 |
| -- 5 | 22200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 254 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 253 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.47 | ||
| vs. Itself - Static | 0.33 | ||
| Wear Factor - Washer | 24.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 7 | 4.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 490 | J/m | ASTM D4812 |
| 23°C 8 | 26 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 0.420 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 279 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 278 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 260 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 266 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 to 316 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 321 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Medalist® MD-34445 NAT XRD1 | Teknor Apex Company | TPE | Medalist® |
| ACCUTECH™ HP0334W30L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Geon™ Vinyl Flexible B5500 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Kemcor LD 4200 Film | Qenos Pty Ltd | LDPE | Kemcor |
| Sylvin 916VO Grey 9153 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |