Shinite® PBT D202
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Shinkong Synthetic Fiber Corp. |
| Trademark: | Shinite® PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zDt7UW_Shinite-PBT-D202.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Shinite® PBT D202 is a Polybutylene Terephthalate (PBT) material. It is available in North America. Important attributes of Shinite® PBT D202 are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 2.0 to 2.2 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.080 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3310 | MPa | ASTM D638 |
| Tensile Strength | 61.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 6.0 | % | ASTM D638 |
| Flexural Modulus | 2760 | MPa | ASTM D790 |
| Flexural Strength | 93.8 | MPa | ASTM D790 |
| Compressive Strength | 100 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 60.0 | °C | ASTM D648 |
| Melting Temperature | 224 | °C | DSC |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Dielectric Constant | 3.00 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 232 to 260 | °C | |
| Middle Temperature | 232 to 260 | °C | |
| Front Temperature | 232 to 260 | °C | |
| Processing (Melt) Temp | 241 to 260 | °C | |
| Mold Temperature | 60.0 to 121 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP513-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Moplen EP380T | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Axiall PVC CL-7049 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Axiall PVC 8640 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Kepital® ES-20 | KEP Americas | Acetal (POM) Copolymer | Kepital® |