SABIC® LDPE HP4027J
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | SABIC Americas, Inc. |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zDglTb_SABIC-LDPE-HP4027J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRODUCT DESCRIPTION: SABlC® LDPE HP4027J is a Low Density Polyethylene grade formulated with slip agent and anti-block additives, with increased density. It typically exhibits excellent draw down ability with higher output. Films typically exhibit good optics, low friction, low blocking and high rigidity. TYPICAL APPLICATIONS: Thin film for textile packaging, high clarity laundry bags, bread bags, general purpose film for high speed automatic packaging lines. This grade is typically suitable where higher stiffness and down gauging are required. This product is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.927 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (0.0500 mm) | 300 | MPa | ISO 527-2 |
| Tensile Stress (yield, 0.0500mm) | 13.0 | MPa | ISO 527-2 |
| Coefficient of Friction | % | ISO 8295 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Blow-up Ratio | 2.00 - 3.00 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Thickness - Recommended / Available | 15 - 40 micron | ||
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 20.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 15.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 300 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 550 | % | ISO 527-3 |
| Dart Drop Impact (50 µm, Blown Film) | 90 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 92.0 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 111 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 20, 50.0 µm, blown film | > 70 | ASTM D2457 | |
| 60, 50.0 µm, blown film | > 110 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | < 8.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Measured on 50 micron thickness blown film extruded at melt temperature of 170°C with BUR of 2.5 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 190 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1005 FR A UV | RTP Company | PBT | RTP |
| TEKAMID™ A210ST | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| TARFLON™ NEO AG2240 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| ExxonMobil™ PP7064L1 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| Sylvin 8250-80LMW Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |