Lustran® Elite 1891
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Styrolution |
| Trademark: | Lustran® Elite |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zDLi0y_Lustran-Elite-1891.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lustran® Elite HH ABS 1891 resin is an injection molding grade of ABS (Acrylonitrile Butadiene Styrene) for high-heat applications in the automotive market. With a Vicat softening temperature of 243°F (117°C)*, Elite HH ABS 1891 provides high heat resistance, low gloss, toughness, and easy flow for processing molded-in color parts. The resin is available in natural and black colors only. Its consistent, clean, natural color makes it ideally suitable for use with color concentrates. Color concentrates for automotive color matches are available from several concentrate suppliers. Lustran Elite HH ABS 1891 resin offers the right balance of properties for a variety of above-the-belt-line automotive applications. It is used for parts in the sun-loaded area where low-gloss, molded-in color is desired. Typical applications include A & B pillars, door panels, sail panels, consoles and console trim, cowl vents, and lamp housings. As with any product, use of Lustran Elite HH ABS 1891 resin in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Specific Volume | 0.950 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 7.0 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 42.1 | MPa | ASTM D638 |
| Yield | 45.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 35 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 2210 | MPa | ASTM D790 |
| -- | 2270 | MPa | ISO 178 |
| Flexural Strength (Yield) | 69.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 190 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 130 | J/m | ASTM D256 |
| 23°C, 12.7 mm | 110 | J/m | ASTM D256 |
| -40°C 1 | 7.6 | kJ/m² | ISO 180/1A |
| 23°C 2 | 17 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 101 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 86.1 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.35mm | 97.2 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 12.7mm | 100 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 117 | °C | ASTM D1525 3 |
| -- | 106 | °C | ISO 306/B50 |
| CLTE - Flow (-30 to 30°C) | 7.9E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 4 | 51 | mm/min | SAE J1685 |
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 87.8 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Shot Size | 50 - 75 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 238 - 254 | °C | |
| Middle Temperature | 243 - 260 | °C | |
| Front Temperature | 249 - 266 | °C | |
| Nozzle Temperature | 249 - 266 | °C | |
| Processing (Melt) Temp | 249 - 271 | °C | |
| Mold Temperature | 48.9 - 71.1 | °C | |
| Injection Pressure | 89.6 - 138 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 44.8 - 103 | MPa | |
| Back Pressure | 0.172 - 0.689 | MPa | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² | |
| Cushion | < 6.35 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Hold Pressure: 50 to 75% of Injection PressureScrew Speed: ModerateDrying at 160°-170°F for 4 hours is also adequate. |
| Note Message | |
|---|---|
| 1 . | 4x10 mm bar |
| 2 . | 4x10 mm bar |
| 3 . | 标准 B (120°C/h), 压 力1 (10N) |
| 4 . | 2x100x355 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 1000 | RTP Company | PBT | RTP |
| Sylvin 8693-65 Clear 8355 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL™ PCN2910 resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |
| INSPIRE™ TF0602S | Trinseo | PP, Unspecified | INSPIRE™ |
| MACOMASS PVC MM-PVC E 1561 | MACOMASS Verkaufs AG | PVC, Flexible | MACOMASS PVC |