Quadrant EPP Techtron® HPV PPS
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zCNFr4_Quadrant-EPP-Techtron-HPV-PPS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Quadrant EPP Techtron® HPV PPS is a Polyphenylene Sulfide (PPS) product filled with filler. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.00 mm | 0.010 | % | |
| Saturation, 23°C | 0.090 | % | |
| Equilibrium, 23°C, 50% RH | 0.030 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 3.00 mm 1 | 0.030 | % | |
| 23°C, 3.00 mm 2 | 2.0 | mg | |
| 23°C, 3.00 mm 3 | 1.0 | mg |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 10.0 mm) | 84 | ISO 2039-2 | |
| Ball Indentation Hardness (10.0 mm) | 180 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4250 | MPa | ISO 527-2/1B/1 |
| Tensile Stress (Break) | 75.0 | MPa | ISO 527-2/1B/5 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2/1B/5 |
| Compressive Stress | ISO 604/1 | ||
| 2% Strain | 55.0 | MPa | |
| 1% Strain | 28.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 25 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 115 | °C | ISO 75-2/A |
| Continuous Use Temperature | |||
| -- 4 | 220 | °C | |
| -- 5 | 260 | °C | |
| Melting Temperature (DSC) | 280 | °C | |
| CLTE - Flow | |||
| 23 to 100°C | 5.0E-5 | cm/cm/°C | |
| 23 to 150°C | 6.0E-5 | cm/cm/°C | |
| > 150°C | 1.0E-4 | cm/cm/°C | |
| Thermal Conductivity (23°C) | 0.30 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 24 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.30 | ||
| 1 MHz | 3.30 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 3.0E-3 | ||
| 1 MHz | 3.0E-3 | ||
| Comparative Tracking Index | 100 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Oxygen Index | 47 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 96 hrs |
| 2 . | Weight, 96 hrs |
| 3 . | Weight, 24 hrs |
| 4 . | 20000 hrs |
| 5 . | Short periods |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinelec CCB6305/G | Teknor Apex Asia Pacific PTE. LTD. | PS (Specialty) | Sinelec |
| THERMOLAST® M TM6LFT (Series: MC/LF) | KRAIBURG TPE | TPE | THERMOLAST® M |
| New-prene™ 9055N-1 | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| Lupoy® 1200-10 | LG Chem Ltd. | PC | Lupoy® |
| Vipel® K026-AAA-00 | AOC, L.L.C. | Vinyl Ester | Vipel® |