Borealis PP ME268AI
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zCGwfu_Borealis-PP-ME268AI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ME268AI is a 20% mineral filled polypropylene compound intended for injection moulding. ME268AI has been developed especially for the car industry to be used in automotive interior parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | 1.1 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 60.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, Injection Molded) | 26.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, Injection Molded) | 5.0 | % | ISO 527-2/50 |
| Flexural Modulus 2(Injection Molded) | 2400 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 37.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C, injection molding | 2.5 | kJ/m² | ISO 179/1eA |
| 23°C, injection molding | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C, injection molding | 30 | kJ/m² | ISO 179/1eU |
| 23°C, injection molding | 70 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C, injection molding | 2.0 | kJ/m² | ISO 180/1A |
| 23°C, injection molding | 5.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -20°C, injection molding | 21 | kJ/m² | ISO 180/1U |
| 23°C, injection molding | 63 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 140 | °C | ISO 306/A |
| -- | 66.0 | °C | ISO 306/B |
| CLTE - Flow 3 | 5.8E-5 | cm/cm/°C | ISO 11359-2 |
| Melt Energy | 57.0 | kJ/kg | ISO 11357 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Atomization- 16 hr (100°C) | mg | DIN 75201 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | µgC/g | VDA 277 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 3.00 - 6.00 | MPa |
| Injection instructions |
|---|
| Feeding temperature: 40 - 80 °CBack pressure: Low to mediumScrew speed: Low to mediumFlow front speed: 100 - 200 m/min |
| Note Message | |
|---|---|
| 1 . | disk |
| 2 . | 2.0 mm/min |
| 3 . | -30°C & 80°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer N63B | Precision Polymer Engineering Ltd. | NBR | Precision Polymer |
| Vyncolit® X658 | Vyncolit N.V. | Phenolic | Vyncolit® |
| Jam PE 526F1 | Jam Petrochemical Company | HDPE | Jam PE |
| LITEN LS 87 | UNIPETROL RPA | PE Copolymer | LITEN |
| LUVOCOM® 65-8570/BL | Lehmann & Voss & Co. | PP Copolymer | LUVOCOM® |