HiFill FR® PA6 GF33 FR HS L
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill FR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zBdWig_HiFill-FR-PA6-GF33-FR-HS-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill FR® PA6 GF33 FR HS L is a Polyamide 6 (Nylon 6) product filled with 33% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.63 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | -- | % | ASTM D955 |
| Water Absorption (24 hr) | 0.75 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength (Break) | 152 | 125 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | 4.5 | % | ASTM D638 |
| Flexural Modulus | 8960 | 6890 | MPa | ASTM D790 |
| Flexural Strength | 200 | 179 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 85 | 120 | J/m | ASTM D256 |
| Unnotched Izod Impact | 850 | 1000 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 218 | -- | °C | |
| 1.8 MPa, Unannealed | 216 | -- | °C | |
| CLTE - Flow | 2.2E-5 | -- | cm/cm/°C | ASTM D696 |
| RTI Elec | 120 | -- | °C | UL 746 |
| RTI Imp | 120 | -- | °C | UL 746 |
| RTI Str | 115 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | -- | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+14 | -- | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 16 | -- | kV/mm | ASTM D149 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.50 mm, ALL) | V-0 | -- | UL 94 |
| Additional Information | Dry | Conditioned | ||
|---|---|---|---|---|
| TPCI # | 6536102 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 232 to 257 | °C | |
| Middle Temperature | 232 to 257 | °C | |
| Front Temperature | 232 to 257 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POWERSIL® 466 A/B | Wacker Chemie AG | Silicone | POWERSIL® |
| Sylvin 9459-73 Black | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |
| Moplen HP565K | LyondellBasell Industries | PP Homopolymer | Moplen |
| Hylon® N2200TL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| Bergamid™ A70 G50 U | PolyOne Corporation | Nylon 66 | Bergamid™ |