Braskem PP H 125
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Braskem |
| Trademark: | Braskem PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zAsgao_Braskem-PP-H-125.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: H 125 is a high melt flow rate homopolymer designed for nonwoven by spunbonded processing. This resin features an excellent processing, allowing increased line speed or air pressure, besides gains on mechanical properties. The narrow molecular weight distribution, special stability and tight gel appearance control, provide its unique performance. Applications: High-performance spunbond nonwovens for hygiene disposables and hospital products; Nonwovens for furniture and decoration; Low-title and/or high-speed spinning multifilaments. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 38 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale, Injection Molded | 103 | ASTM D785 | |
| R-Scale | 103 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Injection Molded) | 33.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Yield, Injection Molded) | 13 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus - 1% Secant | |||
| Injection Molded | 1300 | MPa | ASTM D790 |
| Injection Molded | 1400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, Injection Molded | 25 | J/m | ASTM D256 |
| 23°C, Injection Molded | 2.7 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, Injection Molded | 95.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, Injection Molded | 55.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 154 | °C | ISO 306/A, ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nipol® LX851E | Zeon Corporation | Latex | Nipol® |
| Dryflex® 602450S | ELASTO | SEBS | Dryflex® |
| LNP™ STAT-KON™ TX06488NTX1 compound | SABIC Innovative Plastics | PUR, Unspecified | LNP™ STAT-KON™ |
| Latamid 12 H 90FE03 | LATI S.p.A. | Nylon 12 | Latamid |
| TECHNYL STAR® S 218 V30 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR® |