Durethan® BKV 215 H2.0 DUS035 900051
| Category: | Nylon 6 , Polyamide 66/6 Copolymer |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zAqDS4_DurethanBKV215H20DUS035900051.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.17 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.60 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.80 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.10 | -- | % | ISO 2577 |
| Flow direction : 280°C, 2.00mm 3 | 0.50 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.10 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 7.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 120 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 4300 | 2100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 85.0 | 55.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 4.5 | 15 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 4000 | 2000 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% strain, 23°C | 120 | 55.0 | MPa | ISO 178/A |
| 23°C 6 | 135 | 70.0 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 5.5 | 8.0 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6/66-HI, GHR, 14-040, GF15 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 20 | 35 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | 80 | kJ/m² | ISO 179/1eU |
| 23°C | 70 | 110 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 10 | 10 | kJ/m² | ISO 180/1A |
| 23°C | 20 | 35 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 65 | 60 | kJ/m² | ISO 180/1U |
| 23°C | 60 | 90 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 4.00 | -- | J | ISO 6603-2 |
| 23°C | 10.0 | -- | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 750 | -- | N | ISO 6603-2 |
| 23°C | 1500 | -- | N | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 200 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 175 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | -- | °C | ISO 306/B120 |
| Melting Temperature 8 | 214 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 4.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.5E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 260 - 290 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REVOLVE® N-228 | Matrix Polymers | Plastomer | REVOLVE® |
| Viprene™ P55A-22U-NAT | Alliance Polymers & Services | TPV | Viprene™ |
| Globalene® PF7351 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |
| IDI BMC 44-10 | IDI Composites International | TS, Unspecified | IDI BMC |
| INNOPOL® PP CS 4-8820 GF15 | Inno-Comp Ltd. | PP Random Copolymer | INNOPOL® PP |